UNS S13800 Springs
Home > Products > Springs

We could produce UNS S13800 springs,S13800 springs,S13800 Compression Springs,UNS S13800 Extension Springs,UNS S13800 Torsion Springs,S13800 tension spring, UNS S13800 disc spring, UNS S13800 wave spring,S13800 Spiral Springs,UNS S13800 Automotive Springs,UNS S13800 Elevator Springs,UNS S13800 coil springs,UNS S13800 Conical Springs,UNS S13800 Tapered Springs,UNS S13800 Barrel Springs,S13800 die springs,S13800 Constant Force Springs,S13800 Power Springs,S13800 Garter Springs,UNS S13800 retaining Springs,UNS S13800 Volute Springs,UNS S13800 flat springs,UNS S13800 Volute Springs,UNS S13800 battery springs,UNS S13800 Spring Clips,UNS S13800 Battery Contacts from china

The diameter of UNS S13800 springs that we could do range from 0.30 mm to 3.00 mm.

As per Surface finish of UNS S13800 springs, we could do grinding ,presetting ,deburring ,shot peening ,vibratory finishing ,passivating,painting ,heat setting,stress relief ,end forming,threading ,coining,chamfering ,knurling ,welding ,assembly,grooving ,flatting and so on

As per Coatings of of UNS S13800 springs, we could do chrome,Teflon, corvel,pain,color coding,zinc plating,black oxide,precoated wire and so on

Our UNS S13800 Springs could undergo either bainitic hardening after forming (carbon) or vacuum hardening and annealing (stainless).or come in pre-hardened As per the requirement of the clients

UNS S13800 is a precipitation hardenable stainless. It is a medium to high strength material achieved through appropriate ageing treatments (see table below) and contains very good resistance to stress corrosion.


The chemical composition of S13800 springs is as follows

Chemical Composition (Wt %)


C

Si

Mn

P

S

Cr

Mo

Ni

Al

N

Fe

Min

-

-

-

-

-

12.24

2.00

7.50

0.90

-

Bal

Max

0.05

0.10

0.10

0.01

0.008

13.25

2.50

8.50

1.35

0.010

-



The mechanical property of UNS S13800 spring is as follows

0.2% Proof Stress

Tensile Strength

Elongation

Reduction of Area

Hardnesss

L

T

H900

1413 MPA Min.

1517 MPA Min.

10 % Min.

45 % Min.

35 % Min.

45 HRC Min.

H1000

1310 MPA Min.

1413 MPA Min.

10 % Min.

60 % Min.

40 % Min.

43 HRC Min.

H1025

1207 MPA Min.

1276 MPA Min.

11 % Min.

50 % Min.

45 % Min.

41 HRC Min.

H1050

1138 MPA Min.

1207 MPA Min.

12 % Min.

50 % Min.

45 % Min.

40 HRC Min.

H1100

931 MPA Min.

1034 MPA Min.

14 % Min.

50 % Min.

50 % Min.

34 HRC Min.

H1150

621 MPA Min.

931 MPA Min.

14 % Min.

50 % Min.

50 % Min.

30 HRC Min.


We could do solution treatment and ageing treatment for UNS S13800 springs as per the requirement of the clients.

We could supply inspection certificate of UNS S13800 springs by third party,like TUV,DNV,GL,BV,SGS and so on

We analyze your UNS S13800 spring design and make recommendations to improve quality and reduce cost. Whether you have a sample, drawing or idea, our engineering team is ready to offer you design assistance and material recommendation to best fit your application as well as your budget. We are easy to talk to, well-prepared and ready to put our expertise to work for you.

Our S13800 springs are widely used in Butterfly Valves,Globe Valves,compressed air stream,Agitated Neutsche Filter,Scrubber vessels.Accumulators,Shell and Tube Heat Exchangers,Storage tanks and Handling Equipments,Bulk Liquefied Petroleum Gas (LPG), Propane & Ammonia Storage and Handling Systems,Dry Dock & Ship Yard Maintenance and so on


Please send us the drawing of UNS S13800 springs that you need, we are glad to quote the best price for your side.

Except UNS S13800 Springs,we also could produce UNS S13800 flanges,UNS S13800 plates,UNS S13800 fastener,UNS S13800 bolts,UNS S13800 fittings,UNS S13800 pipes,UNS S13800 tubes,UNS S13800 bars