Ph13-8Mo Springs
Home > Products > Springs

We could produce Ph13-8Mo springs,Ph 13-8 Mo springs,Ph 13-8 Mo Compression Springs,Ph13-8Mo Extension Springs,Ph13-8Mo Torsion Springs,Ph 13-8 Mo tension spring, Ph13-8Mo disc spring, Ph13-8Mo wave spring,Ph 13-8 Mo Spiral Springs,Ph13-8Mo Automotive Springs,Ph13-8Mo Elevator Springs,Ph13-8Mo coil springs,Ph13-8Mo Conical Springs,Ph13-8Mo Tapered Springs,Ph13-8Mo Barrel Springs,Ph 13-8 Mo die springs,Ph 13-8 Mo Constant Force Springs,Ph 13-8 Mo Power Springs,Ph 13-8 Mo Garter Springs,Ph13-8Mo retaining Springs,Ph13-8Mo Volute Springs,Ph13-8Mo flat springs,Ph13-8Mo Volute Springs,Ph13-8Mo battery springs,Ph13-8Mo Spring Clips,Ph13-8Mo Battery Contacts from china
The diameter of Ph13-8Mo springs that we could do range from 0.30 mm to 3.00 mm.
Our Ph13-8Mo springs come in a variety of surface finishes from bluing to clear or yellow zinc electroplating, electrolytic nickel, powder coating and zinc phosphate coating always executed by specialized subcontractors
At the end of the manufacturing and stress relief cycles, clients require different and very specific types of treatments in order to improve Ph13-8Mo spring performance. Terminal coil grinding, spring setting, internal and external tumbling, shot peen and vibration are the most common ones.
Ph13-8Mo is a precipitation hardenable, martensitic stainless steel

The chemical composition of Ph 13-8 Mo springs is as follows

Chemical Composition (Wt %)



C

Si

Mn

P

S

Cr

Mo

Ni

Al

N

Fe

Min

-

-

-

-

-

12.24

2.00

7.50

0.90

-

Bal

Max

0.05

0.10

0.10

0.01

0.008

13.25

2.50

8.50

1.35

0.010

-


The mechanical property of Ph13-8Mo spring is as follows


0.2% Proof Stress

Tensile Strength

Elongation

Reduction of Area

Hardnesss





L

T


H900

1413 MPA Min.

1517 MPA Min.

10 % Min.

45 % Min.

35 % Min.

45 HRC Min.

H1000

1310 MPA Min.

1413 MPA Min.

10 % Min.

60 % Min.

40 % Min.

43 HRC Min.

H1025

1207 MPA Min.

1276 MPA Min.

11 % Min.

50 % Min.

45 % Min.

41 HRC Min.

H1050

1138 MPA Min.

1207 MPA Min.

12 % Min.

50 % Min.

45 % Min.

40 HRC Min.

H1100

931 MPA Min.

1034 MPA Min.

14 % Min.

50 % Min.

50 % Min.

34 HRC Min.

H1150

621 MPA Min.

931 MPA Min.

14 % Min.

50 % Min.

50 % Min.

30 HRC Min.


We could do solution treatment and ageing treatment for Ph13-8Mo springs as per the requirement of the clients.
We could supply inspection certificate of Ph13-8Mo springs by third party,like TUV,DNV,GL,BV,SGS and so on
In order to control the quality of Ph 13-8 Mo springs, we have following inspection equipment:Magnetic Particle Flaw Detector,Hot Coil Spring Production Line.Fatigue Testing Machine,Hardening Furnace,Optical Emission Spectrometry,Spring Coiler,Salt Spray Test Machine,Shot Blaster Machine,Automatic Spring Coiler,Electric Temper Furnace,Electric Temper Furnace,Automatic Spring Coiler,Pressure Testing Machine 20mm CNC Spring Coiler,Spring Grinder,Pressure Testing Machine
Our Ph 13-8 Mo springs are widely used in Quarry & Opencast Mine Maintenance ,Mining & Excavation Plant Equipment ,Deep Mining Pit Maintenance & Repair ,Conveyor Equipment Manufacturers .Mine Construction & Site Extension Construction Impact, Jaw & Cone Crusher Manufacturers,Drilling, Scalping & Screener Equipment Manufacturers and so on

Please send us the drawing of Ph13-8Mo springs that you need, we are glad to quote the best price for your side.
Except Ph13-8Mo Springs,we also could produce Ph13-8Mo flanges,Ph13-8Mo plates,Ph13-8Mo fasteners,Ph13-8Mo bolts,Ph13-8Mo pipe fittings,Ph13-8Mo pipes,Ph13-8Mo tubes,Ph13-8Mo bars