UNS N30035 Pipes
Home > Products > Pipes

We could produce UNS N30035 pipes,N30035 pipes,UNS N30035 seamless pipes,UNS N30035 welded pipes,UNS N30035 boiler pipes, UNS N30035 heat exchanger pipes,UNS N30035 Capillary pipes,N30035 Thermocouple pipes,UNS N30035 Superheater pipes and reheater pipes,UNS N30035 condenser pipe,UNS N30035 finned pipes,N30035 furnace pipes,UNS N30035 instrumentation pipes,UNS N30035 Evaporator pipes,UNS N30035 honed pipes,N30035 coiled pipes,UNS N30035 Precision pipes,UNS N30035 High pressure pipes,UNS N30035 hydraulic pipes from china

The outer diameter of UNS N30035 pipes that we could do is from 0.4MM to 850MM,The thickness of UNS N30035 that we could do is from 0.12MM to 100MM

We could meet size tolerance for UNS N30035 Pipes is as follows:OD : + ± 0.5% of specified diameter based on circumferential measurement. Thick : Minimum thickness at any point not more than 0.3 mm under nominal thi,Out of Roundness : difference between maximum and minimum OD 1% ,Straightness : 3 mm in 3 mtrs

Length : As per customer specification

As per surface finish of N30035 pipes, we could do pickled and polish into bright surface as per the requirement of the clients, also for bright surface of UNS N30035 pipes, we could meet 2D finish.No. 4 Finish,No. 6 Finish,No. 7 Finish as per the requirement of the clients

UNS N30035 is an age hardenable Nickel-Cobalt base alloy that has a unique combination of properties - ultra high strength, toughness, ductility and outstanding corrosion resistance


The chemical composition of UNS N30035 pipes is as follows

Type Analysis

Single figures are nominal except where noted.

Carbon (Maximum)

0.02

%

Manganese (Maximum)

0.15

%

Phosphorus (Maximum)

0.015

%

Sulfur (Maximum)

0.010

%

Silicon (Maximum)

0.15

%

Chromium

19.00 to 21.00

%

Nickel

33.00 to 37.00

%

Molybdenum

9.00 to 10.50

%

Cobalt

Balance

Titanium (Maximum)

1.00

%

Boron

0.010

%

Iron (Maximum)

1.00

%



The mechanical propery of N30035 seamless pipes is as follows

Material

Condtion

Ultimate  Tensile Strength PSI

0.2 %  Yield Strength PSI

Elongation  %

Reduction  of Area %

Hardness  HRC

UNS  R30035

Solution  Heat Treated and Work Strengthened

253170

253170

12

50

45


As per heat treatment of UNS N30035 pipes, we could do solution treatment, annealed treatment as per the requirement of the clients

As per material of UNS N30035 pipes, our raw material has been melted by  EAF+VOD-ESR methods

We produce UNS N30035 seamless pipes and weled pipes as per the standard of ASTM B729 and ASTM B464

We will do Destructive testing for our every piece of UNS N30035 seamless pipes and weled pipes:such as tensile tests (including hot tensile testing),impact tests (up to -196 degrees Celsius),bend tests,hardness tests,intercrystalline corrosion test in accordance with ASTM A262 practice E,pitting corrosion test in accordance with ASTM G48A,metallurgical tests (metal analysis, macro & micro examination)

We ALso do Non-destructive testing for our every piece of UNS N30035 seamless pipes and weled pipes:such as eddy current testing,ultrasonic testing,hydro testing,x-ray testing (radiographic & radioscopic),positive material indentification testing

Our UNS N30035 pipes are packed wooden crates lined with wax craft paper, tri-wall clay-coated reinforced cases

Our UNS N30035 seamless pipe and weled pipes are widely used in many industry :Boilers,Bridges,Construction Machinery,Engineered Plumbing,Engines,Hydraulics,Impellers,Jewelry,Machine Tools,Water Treatment Plants and so on


Our UNS N30035 seamless pipe and weled pipes could be by Third party approvals,such as American Bureau of Shipping,Bureau Veritas,Det Norske Veritas,Germanischer Lloyd,Lloyd's Register,PED and so on

Please send us the size and quantity of UNS N30035 pipes that you need, we are glad to quote the best price for your side

Except UNS N30035 pipes,we also could produce UNS N30035 flanges,UNS N30035 plates,UNS N30035 fastener,UNS N30035 bolts,UNS N30035 fittings,UNS N30035 bars,UNS N30035 tubes,UNS N30035 springs