Ph13-8Mo Pipes
Home > Products > Pipes

We could produce Ph13-8Mo pipes,Ph 13-8 Mo pipes,Ph13-8Mo seamless pipes,Ph13-8Mo welded pipes,Ph13-8Mo boiler pipes, Ph13-8Mo heat exchanger pipes,Ph13-8Mo Capillary pipes,Ph 13-8 Mo Thermocouple pipes,Ph13-8Mo Superheater pipes and reheater pipes,Ph13-8Mo condenser pipe,Ph13-8Mo finned pipes,Ph 13-8 Mo furnace pipes,Ph13-8Mo instrumentation pipes,Ph13-8Mo Evaporator pipes,Ph13-8Mo honed pipes,Ph 13-8 Mo coiled pipes,Ph13-8Mo Precision pipes,Ph13-8Mo High pressure pipes,Ph13-8Mo hydraulic pipes from china
The outer diameter of Ph13-8Mo pipes that we could do is from 0.4MM to 850MM,The thickness of Ph13-8Mo that we could do is from 0.12MM to 100MM
As per surface finish of Ph 13-8 Mo pipes, we could do pickled and polish into bright surface as per the requirement of the clients, also for bright surface of Ph13-8Mo pipes, we could meet 2D finish.No. 4 Finish,No. 6 Finish,No. 7 Finish as per the requirement of the clients
Ph13-8Mo is a precipitation hardenable, martensitic stainless steel which combines a high level of corrosion resistance and high strength coupled with superior toughness and transverse mechanical properties.

The chemical composition of Ph13-8Mo pipes is as follows

Element

Min

Max

C

-

0.05

Si

-

0.10

Mn

-

0.10

P

-

0.010

S

-

0.008

Cr

12.25

13.25

Mo

2.00

2.50

Ni

7.50

8.50

Al

0.90

1.35

N

-

0.010

Fe

Bal

-


The mechanical propery of Ph 13-8 Mo seamless pipes is as follows


0.2% Proof Stress

Tensile Strength

Elongation

Reduction of Area

Hardnesss





L

T


H900

1413 MPA Min.

1517 MPA Min.

10 % Min.

45 % Min.

35 % Min.

45 HRC Min.

H1000

1310 MPA Min.

1413 MPA Min.

10 % Min.

60 % Min.

40 % Min.

43 HRC Min.

H1025

1207 MPA Min.

1276 MPA Min.

11 % Min.

50 % Min.

45 % Min.

41 HRC Min.

H1050

1138 MPA Min.

1207 MPA Min.

12 % Min.

50 % Min.

45 % Min.

40 HRC Min.

H1100

931 MPA Min.

1034 MPA Min.

14 % Min.

50 % Min.

50 % Min.

34 HRC Min.

H1150

621 MPA Min.

931 MPA Min.

14 % Min.

50 % Min.

50 % Min.

30 HRC Min.


As per heat treatment of Ph13-8Mo pipes, we could do solution treatment, annealed treatment as per the requirement of the clients
As per material of Ph13-8Mo pipes, our raw material has been melted by  EAF+VOD-ESR methods
We produce Ph13-8Mo seamless pipes and weled pipes as per the standard of ASTM B729 and ASTM B464
In order to control the quality of Ph 13-8 Mo seamless pipes and weled pipes, we will do Positive material identification (PMI),Visual inspection,Dimensional inspection.Laser micrometer inspection,Destructive testing( includes tensile, hardness, bending, flattening, flare and metallurgical tests),ultrasonic testing and pressure testing,Liquid Penetrate testing as per the requirement of the clients
Our Ph13-8Mo pipes are packed wooden crates lined with wax craft paper, tri-wall clay-coated reinforced cases
Our Ph13-8Mo seamless pipe and weled pipes are widely used in many industry :Tanks & Vessels.Fluid Transfer Systems.Heat Transfer Systems,Plant Maintenance & Refurbishment Subcontractors.Separation Systems & Equipment Manufacturers,Biochemical Plant Equipment Manufacturers,Chemical Processing Equipment Manufacturers.Feedstock Processing Equipment Manufacturers,Pressure Vessel Manufacturers.Filtration Systems and so on

We could supply Ph13-8Mo pipe material certificate as per En10204-3.1 or EN10204-3.2 by third parts(like TUV,DNV,GL,and so on)
Please send us the size and quantity of Ph13-8Mo pipes that you need, we are glad to quote the best price for your side
Except Ph13-8Mo pipes,we also could produce Ph13-8Mo flanges,Ph13-8Mo plates,Ph13-8Mo fasteners,Ph13-8Mo bolts,Ph13-8Mo pipe fittings,Ph13-8Mo bars,Ph13-8Mo tubes,Ph13-8Mo springs