2.4668 Pipes
Home > Products > Pipes

We could produce 2.4668 pipes,EN 2.4668 pipes,2.4668 seamless pipes,2.4668 welded pipes,2.4668 boiler pipes, 2.4668 heat exchanger pipes,2.4668 Capillary pipes,EN 2.4668 Thermocouple pipes,2.4668 Superheater pipes and reheater pipes,2.4668 condenser pipe,2.4668 finned pipes,EN 2.4668 furnace pipes,2.4668 instrumentation pipes,2.4668 Evaporator pipes,2.4668 honed pipes,EN 2.4668 coiled pipes,2.4668 Precision pipes,2.4668 High pressure pipes,2.4668 hydraulic pipes from china

The outer diameter of 2.4668 pipes that we could do is from 0.4MM to 850MM,The thickness of 2.4668 that we could do is from 0.12MM to 100MM

We could meet size tolerance for 2.4668 Pipes is as follows:OD : + ± 0.5% of specified diameter based on circumferential measurement. Thick : Minimum thickness at any point not more than 0.3 mm under nominal thi,Out of Roundness : difference between maximum and minimum OD 1% ,Straightness : 3 mm in 3 mtrs

Length : As per customer specification

As per surface finish of EN 2.4668 pipes, we could do pickled and polish into bright surface as per the requirement of the clients, also for bright surface of 2.4668 pipes, we could meet 2D finish.No. 4 Finish,No. 6 Finish,No. 7 Finish as per the requirement of the clients

2.4668 is a precipitation hardenable nickel-based alloy  


The chemical composition of 2.4668 pipes is as follows

Nickel

Iron

Chromium

Copper

Molybdenum

Niobium

Carbon

Manganesew

50.00-55.00

Remainder

17.00-21.00

.30 max

2.80-3.30

4.75-5.50

.08 max

.35 max

Phosphorous

Sulfur

Silcon

Titanium

Aluminimum

Cobalt

Boron

.015 max

.015 max

.35 max

.65-1.15

.20-.80

1.00 max

.006 max


The mechanical propery of EN 2.4668 seamless pipes is as follows

Ultimate Tensile Strength, psi

.2% Yield Strength psi

Elongation %

Hardness Rockwell B

1034Mpa

827Mpa

20

298-363 HB


As per heat treatment of 2.4668 pipes, we could do solution treatment, annealed treatment as per the requirement of the clients

As per material of 2.4668 pipes, our raw material has been melted by  EAF+VOD-ESR methods

We produce 2.4668 seamless pipes and weled pipes as per the standard of ASTM B729 and ASTM B464

We will do Destructive testing for our every piece of 2.4668 seamless pipes and weled pipes:such as tensile tests (including hot tensile testing),impact tests (up to -196 degrees Celsius),bend tests,hardness tests,intercrystalline corrosion test in accordance with ASTM A262 practice E,pitting corrosion test in accordance with ASTM G48A,metallurgical tests (metal analysis, macro & micro examination)

We ALso do Non-destructive testing for our every piece of 2.4668 seamless pipes and weled pipes:such as eddy current testing,ultrasonic testing,hydro testing,x-ray testing (radiographic & radioscopic),positive material indentification testing

Our 2.4668 pipes are packed wooden crates lined with wax craft paper, tri-wall clay-coated reinforced cases

Our 2.4668 seamless pipe and weled pipes are widely used in many industry :Feed-water and steam generator tubing in power plants,Brine heaters and evaporator bodies in salt plants,Sulphuric and hydrouoric acid alkylation plants,Industrial heat exchangers,Cladding for crude oil distillation columns,Splash-zone sheathing in offshore structures, seawater service,Plants for isotope separation in the production of nuclear fuel pumps and valves used in the manufacture of chlorinated hydrocarbons and so on


Our 2.4668 seamless pipe and weled pipes could be by Third party approvals,such as American Bureau of Shipping,Bureau Veritas,Det Norske Veritas,Germanischer Lloyd,Lloyd's Register,PED and so on

Please send us the size and quantity of 2.4668 pipes that you need, we are glad to quote the best price for your side

Except 2.4668 pipes,we also could produce 2.4668 flanges,2.4668 plates,2.4668 fastener,2.4668 bolts,2.4668 fittings,2.4668 bars,2.4668 tubes,2.4668 springs