We are professional A182-F6nm(UNS S41500,1.4313,X3CrNiMo13-4)Forged Forging Steel Turbine Francis Hydro Power Hydraulic Turbine Generator Wicked Wicket Gates blades Guide vanes ASTM A182-F6NM Grade F6NM ASTM A182 Gr F6nm F 6NM from china
Wicket gate plays an important role in hydropower plants. Wicket gate increases turbine revolution and after paralleling with net, increases the turbine load. Changing in turning place of this part causes the change in flow rate of turbine runner. Wicket gate conducts the water flow into runner. In this case, the angle of entering water to runner is too important and plays an important role in efficiency and reducing cavitations.0005.jpg
Because of nature of flowing water in turbine direction, sandy parcels and impure material, and cavitations causes friction and corrosion in wicket gates. So after a time depend on the condition of operation and the water and grease material, the journal place and the sealing on the wicket will corrode.
In this case, manufacturing and and/or purchasing a new wicket gate is too expensive and needs much time, so AzarAb tries to use certain economical maintenance methods and makes the start to power plants easy.
Based on following applicable method wicket gates can be ready to perform in a short time: total wicket gate cleaning, quality control in all levels repairing the ruined parts, cleaning the welding surfaces, thermal operation for stress – relief, make the repaired surfaces to standard sizes by lathe operation, doing chrome campsite coating in friction surfaces and wicket gates seats.
The machining operation of wicket gate is too important in a way that shaft and seat angle of the sealing should be in the same direction.
Chemical composition of F6NM
C | Si | Mn | P | S | Cr | Ni | Mo | Fe | |
---|---|---|---|---|---|---|---|---|---|
Min | • | • | 0.50 | • | • | 11.50 | 3.50 | 0.50 | 0.00 |
Max | 0.05 | 0.60 | 1.00 | 0.030 | 0.030 | 14.00 | 5.50 | 1.00 | 0.00 |
Mechanical properties of F6NM
Condition: Hardened and Double Tempered
U.T.S | 95 KSI Min | (655 N/mm2) |
---|---|---|
0.2% Proof Stress | 75 KSI Min | (517 N/mm2) |
Elongation | 18 % | |
Red of Area | 35 % | |
CVN Impacts @ -60°C (-75°F) | 40 Joules | (30 ft-lbf) |
-
New
·1.4898 Bars ·1.4886 Bars ·1.4529 Bars ·1.4876 Bars ·2.4856 Bars ·2.4851 Bars ·2.4816 Bars ·2.4668 Bars ·2.4663 Bars ·2.4642 Bars -
Any
·UNS N04404 Bars ·UNS N06007 Bars ·UNS S31635 Bars ·UNS N06690 Bars ·Hastelloy B-3 Bars ·UNS N06950 Bars ·UNS S24100 Bars ·UNS N06455 Bars ·A182-F61 Bars ·Custom 465 Bars -
Hot
·Inconel 600 Bars ·Inconel 601 Bars ·Inconel 617 Bars ·Inconel 625 Bars ·Inconel 686 Bars ·Inconel 690 Bars ·Inconel 693 Bars ·Inconel 718 Bars ·Inconel 725 Bars ·Inconel 751 Bars